PPS or Polyphenylene Sulfide was first developed in the 1960s as a high-performance polymer. It bridges the gap between standard plastics and advanced materials, offering unique properties that make it essential in various industries.
In this post, we'll explore PPS's unique properties, diverse applications, how processing, and why it's becoming indispensable in various industries.
Polyphenylene sulfide (PPS) offers high-temperature resistance, rigidity, and an opaque appearance as a semi-crystalline thermoplastic.
The backbone of PPS consists of para-phenylene units alternating with sulfide linkages. This gives PPS its characteristic properties.
Repeating Unit: -[C6H4-S]n-
C6H4 represents the benzene ring
S is a sulfur atom
Sulfur atoms form single covalent bonds between benzene rings. They connect in a para (1,4) configuration, creating a linear chain.
PPS forms semi-crystalline structures, contributing to its thermal stability and chemical resistance.
The unit cell of PPS is orthorhombic, with the following dimensions:
a = 0.867 nm
b = 0.561 nm
c = 1.026 nm
The calculated heat of fusion for an ideal PPS crystal is 112 J/g. This structure gives PPS its high melting point of 280°C.
The degree of crystallinity in PPS ranges from 30% to 45%. It depends on:
Thermal history
Molecular weight
Cross-linked status (linear or not)
Higher crystallinity increases:
Strength
Stiffness
Chemical resistance
Heat resistance
Lower crystallinity improves:
Impact resistance
Elongation
You can prepare amorphous and crosslinked PPS by:
Heating above melting temperature
Cooling to 30°C below melting point
Holding for hours in air presence
This structure gives PPS excellent properties like high-temperature resistance and chemical inertness.
PPS resin comes in different forms, each with unique properties tailored for specific applications.
Linear PPS
Has nearly double the molecular weight of regular PPS
Results in higher tenacity, elongation, and impact strength
Cured PPS
Produced by heating regular PPS in the presence of air (O2)
Curing extends molecular chains and creates some branches
Enhances molecular weight and provides thermoset-like characteristics
Branched PPS
Has a higher molecular weight than regular PPS
Features extended polymer chains branching off the backbone
Improves mechanical properties, tenacity, and ductility
The table below compares the molecular weight of different PPS types:
| PPS Type | Molecular Weight Comparison |
|---|---|
| Regular PPS | Baseline |
| Linear PPS | Nearly double regular PPS |
| Cured PPS | Increased from regular PPS due to chain extension and branching |
| Branched PPS | Higher than regular PPS |
The molecular weight of PPS plays a crucial role in determining its properties. Higher molecular weight generally leads to:
Improved mechanical strength
Better impact resistance
Increased ductility and elongation
However, it can also result in increased viscosity, making processing more challenging.
PPS plastic exhibits a unique combination of properties that make it suitable for various applications.
PPS boasts outstanding mechanical properties, making it ideal for demanding applications.
Tensile Strength: With a tensile strength of 12,500 psi (86 MPa), PPS can withstand significant loads without breaking.
Impact Resistance: Despite its rigidity, PPS has an Izod impact strength of 0.5 ft-lbs/in (27 J/m), allowing it to absorb sudden shocks.
Flexural Modulus of Elasticity: At 600,000 psi (4.1 GPa), PPS effectively resists bending forces, maintaining its shape and structural integrity.
Dimensional Stability: PPS maintains its dimensions even under high temperature and humidity conditions, making it suitable for precision parts with tight tolerances.
PPS excels in thermal stability and resistance, crucial for high-temperature applications.
Heat Deflection Temperature: PPS can withstand temperatures up to 260°C (500°F) at 1.8 MPa (264 psi) and 110°C (230°F) at 8.0 MPa (1,160 psi).
Coefficient of Linear Thermal Expansion: PPS shows minimal dimensional changes with temperature variations at 4.0 × 10⁻⁵ in/in/°F (7.2 × 10⁻⁵ m/m/°C).
Maximum Continuous Service Temperature: PPS can be used continuously in air at temperatures up to 220°C (428°F).
PPS is known for its exceptional chemical resistance, making it suitable for harsh environments.
Resistance to Moisture: PPS remains unaffected by moisture, ensuring durability and reliability in humid conditions.
Resistance to Various Chemicals: PPS withstands exposure to aggressive chemicals, including strong acids, bases, organic solvents, oxidizing agents, and hydrocarbons.
PPS's electrical insulation properties make it suitable for electronic applications.
High Volume Resistivity: PPS maintains high insulation resistance even in high-humidity environments, with a volume resistivity of 10⊃1;⁶ Ω·cm.
Dielectric Strength: With a dielectric strength of 450 V/mil (18 kV/mm), PPS ensures excellent insulation.
PPS offers several other desirable properties:
Flame Resistance: Most PPS compounds pass the UL94V-0 standard without additional flame retardants.
High Modulus When Reinforced: Reinforced PPS grades exhibit a high modulus, enhancing mechanical strength.
Low Water Absorption: With a water absorption of just 0.02% after 24 hours of immersion, PPS is ideal for applications requiring minimal moisture uptake.
The following table summarizes the key properties of PPS plastic:
| Property | Value |
|---|---|
| Tensile Strength (ASTM D638) | 12,500 psi (86 MPa) |
| Izod Impact Strength (ASTM D256) | 0.5 ft-lbs/in (27 J/m) |
| Flexural Modulus (ASTM D790) | 600,000 psi (4.1 GPa) |
| Heat Deflection Temperature (ASTM D648) | 500°F (260°C) @ 264 psi |
| Coefficient of Linear Thermal Expansion | 4.0 × 10⁻⁵ in/in/°F |
| Maximum Continuous Service Temperature | 428°F (220°C) |
| Volume Resistivity (ASTM D257) | 10⊃1;⁶ Ω·cm |
| Dielectric Strength (ASTM D149) | 450 V/mil (18 kV/mm) |
| Water Absorption (ASTM D570, 24h) | 0.02% |
These properties make PPS an excellent choice for applications demanding high performance, durability, and reliability in challenging environments.
The PPS story began in 1967 with Edmonds and Hill at Philips Petroleum. They developed the first commercial process under the brand name Ryton.
Key features of the original process:
Produced low molecular weight PPS
Ideal for coating applications
Required curing for molding grades
Today's PPS production has evolved significantly. Modern processes aim to:
Eliminate the curing stage
Develop products with improved mechanical strength
Increase efficiency and reduce environmental impact
PPS production involves a clever bit of chemistry. Here's the basic recipe:
Mix sodium sulfide and dichlorobenzene
Add a polar solvent (e.g., N-methylpyrrolidone)
Heat to about 250°C (480°F)
Watch the magic happen!
Curing is crucial for molding grade PPS. It happens around the melting point with a dash of air.
Effects of curing:
Increases molecular weight
Boosts toughness
Reduces solubility
Decreases melt flow
Lowers crystallinity
Darkens color (hello, brownish hue!)
Polar solvents are the unsung heroes of PPS production. They:
Facilitate the reaction between sodium sulfide and dichlorobenzene
Help control the polymer's molecular weight
Influence the final properties of PPS
Common polar solvents used:
N-methylpyrrolidone (NMP)
Diphenyl sulfone
Sulfolane
Each solvent brings its own flavour to the PPS party, affecting the final product's characteristics.
PPS plastic finds use in various industries due to its unique combination of properties.
In the automotive and aerospace sectors, PPS is used for components requiring durability, heat resistance, and chemical stability.
Engine Components: PPS is used in connectors, housings, and thrust washers, where its high-temperature resistance and mechanical strength are crucial.
Fuel System Parts: PPS components are used in fuel systems because of their chemical resistance and ability to withstand high temperatures.
Aircraft Interiors: PPS is found in aircraft ducting components and interior brackets, where its lightweight and durable nature is advantageous.
PPS's electrical insulation properties make it ideal for electronic and electrical applications.
Connectors and Insulators: PPS is used in connectors and insulators due to its high dielectric strength and thermal stability.
Circuit Boards: PPS finds use in circuit boards, supporting miniaturization and high performance.
Microelectronics Applications: PPS is suitable for microelectronics applications, offering excellent dimensional stability and insulation properties.
PPS's chemical resistance makes it suitable for components exposed to corrosive chemicals.
Valves and Pumps: PPS is used in valves, pumps, and fittings in chemical processing applications because it withstands aggressive chemicals at elevated temperatures.
Filter Housings: PPS is used in filter housings, ensuring durability and chemical resistance in filtration systems.
Seals and Gaskets: PPS is ideal for seals and gaskets in chemical environments, providing long-lasting performance and resistance to degradation.
PPS is employed in industrial equipment for its wear resistance and mechanical strength.
Gears and Bearings: PPS is used in gears, bearings, and other wear-resistant components requiring high mechanical strength and dimensional stability.
Compressor Components: PPS is used in compressor vanes because it offers high strength and durability in demanding industrial applications.
Wear-Resistant Applications: PPS components are utilized in wear bands and bushings, providing low friction and high wear resistance in industrial machinery.
PPS finds application in the semiconductor industry due to its purity and insulation properties.
Semiconductor Machinery Components: PPS is used in connectors, contact rails, heat shields, and contact pressure discs in semiconductor production equipment.
Special Grades for Semiconductor Applications: Specialty PPS grades like TECATRON SE and SX are designed for semiconductor applications, offering high purity and enhanced properties.
PPS is used in various mechanical engineering applications.
Compressor and Pump Parts: PPS is used in compressor and pump components due to its chemical resistance and mechanical strength.
Chain Guides and Base Plates: PPS finds use in chain guides and base plates, providing wear resistance and dimensional stability.
PPS plastic is used in several other industries:
Textile Machinery: PPS components are used in dyeing, printing, and processing equipment, offering durability and chemical resistance.
Medical Devices: PPS is used in surgical instrument parts due to its chemical resistance and ability to withstand sterilization processes.
Oil and Gas Equipment: PPS is used in downhole equipment, seals, and connectors, where its chemical resistance and high-temperature stability are essential.
The following table summarizes the key applications of PPS plastic across various industries:
| Industry | Applications |
|---|---|
| Automotive and Aerospace | Engine components, fuel system parts, aircraft interiors |
| Electronics | Connectors, insulators, circuit boards, microelectronics |
| Chemical Processing | Valves, pumps, filter housings, seals, gaskets |
| Industrial Equipment | Gears, bearings, compressor components, wear-resistant parts |
| Semiconductor | Machinery components, special grades for semiconductor production |
| Mechanical Engineering | Compressor and pump parts, chain guides, base plates |
| Textile | Dyeing and printing equipment, processing machinery |
| Medical | Surgical instrument parts |
| Oil and Gas | Downhole equipment, seals, connectors |
Various additives and reinforcements can be used to enhance the properties of PPS plastic.
Glass Fiber Reinforcement
Glass fibers increase the tensile strength, flexural modulus, and dimensional stability of PPS.
They make PPS suitable for applications requiring high mechanical strength.
Standard compounds like PPS-GF40 and PPS-GF MD 65 have a significant market share.
Carbon Fiber Reinforcement
Carbon fibers improve the stiffness and thermal conductivity of PPS.
They enhance PPS's performance in high-temperature applications.
PTFE Additives
PTFE additives reduce the coefficient of friction of PPS.
They make PPS ideal for bearing and wear applications.
Nanoparticles and Nanocomposites
PPS-based nanocomposites can be prepared using carbon nanofillers (e.g., expanded graphite, carbon nanotubes) or inorganic nanoparticles.
Nanofillers are added to PPS primarily to improve its mechanical properties.
Most PPS nanocomposites have been prepared by melt-blending due to PPS's insolubility in common organic solvents.
The following table compares the properties of unfilled, glass-reinforced, and glass-mineral filled PPS:
| Property (Unit) | Unfilled | Glass Reinforced (40%) | Glass-Mineral Filled* |
|---|---|---|---|
| Density (kg/l) | 1.35 | 1.66 | 1.90 - 2.05 |
| Tensile Strength (MPa) | 65-85 | 190 | 110-130 |
| Elongation at Break (%) | 6-8 | 1.9 | 1.0-1.3 |
| Flexural Modulus (MPa) | 3800 | 14000 | 16000-19000 |
| Flexural Strength (MPa) | 100-130 | 290 | 180-220 |
| Izod Notched Impact Strength (kJ/m²) | - | 11 | 5-6 |
| HDT/A @ 1.8 MPa (°C) | 110 | 270 | 270 |
*Depending on the glass/mineral filler ratio
Specific additives can be used to target and enhance particular properties of PPS:
Alkali Metal Silicates for Viscosity Control
Alkali metal silicates, alkali metal sulfites, amino acids, and oligomers of a silyl ether can be used to control the melt flow and viscosity of PPS.
Calcium Chloride for Molecular Weight Increase
Adding calcium chloride during the polymerization process can increase the molecular weight of PPS.
Block Copolymers for Impact Resistance Improvement
Including block copolymers in the initial reaction can improve the impact resistance of PPS.
Sulfonic Acid Esters for Crystallization Rate Enhancement
Adding sulfonic acid esters along with a nucleating agent can improve the crystallization rate of PPS.
The following table summarizes the additives used for specific property enhancements:
| Property Requirement | Suitable Additives |
|---|---|
| Low melt flow, high viscosity | Alkali metal silicates, alkali metal sulfites, amino acids, oligomers of a silyl ether |
| Increased molecular weight | Calcium chloride added during polymerization |
| Improved impact resistance | Inclusion of block copolymers in the initial reaction |
| Increased crystallization rate | Sulfonic acid esters along with a nucleating agent |
| Increased heat stability, low crystallization temperature | Alkali metal or alkali earth metal dithionate |
PPS resins can be processed using various techniques, including injection molding, extrusion, blow molding, and machining.
Injection molding is a common processing method for PPS, offering high productivity and precision.
Pre-drying Requirements
PPS should be pre-dried at 150-160°C for 2-3 hours or 120°C for 5 hours.
This prevents moisture-related issues and enhances the molded appearance.
Temperature and Pressure Settings
The recommended cylinder temperature for PPS is 300-320°C.
Mold temperatures should be maintained between 120-160°C to ensure good crystallization and minimize warping.
An injection pressure of 40-70 MPa is suitable for optimal results.
A screw speed of 40-100 rpm is recommended for PPS.
Mold Considerations
Due to PPS's low viscosity, mold tightness must be checked to prevent leakage.
For filled PPS grades, a higher processing temperature should be used to avoid wear on the barrel, screw, and screw tip.
PPS can be extruded into various shapes, such as fibers, films, rods, and slabs.
Drying Conditions
PPS should be pre-dried at 121°C for 3 hours to ensure proper moisture control.
Temperature Control
The melt temperature range for PPS extrusion is 290-325°C.
Mold temperatures should be maintained between 300-310°C for optimal results.
Applications in Fiber and Film Production
PPS is commonly extruded for fiber and monofilament production.
It is also used to produce tubing, rods, and slabs.
PPS can be processed using blow molding techniques.
Temperature Ranges and Considerations
The recommended processing temperature range for blow molding PPS is 300-350°C.
Higher temperatures may be required for filled PPS grades to avoid equipment wear.
PPS is highly machinable, allowing for precise and complex part fabrication.
Coolant Selection
Non-aromatic, water-soluble coolants, such as pressurized air and spray mists, are ideal for achieving high-quality surface finishes and close tolerances.
Annealing Process
Stress-relieving through an annealing process at controlled temperatures is recommended to reduce surface cracks and internal stresses.
Achieving Precision in Complex Parts
PPS can be machined to close tolerances, making it suitable for complex, precision parts.
Pre-drying PPS is crucial for achieving optimal processing results.
Effect on Molded Product Appearance
Pre-drying enhances the molded appearance of PPS products.
It prevents moisture-related defects, such as surface imperfections and bubbles.
Prevention of Drooling During Processing
Proper pre-drying prevents drooling during processing.
Drooling can cause inconsistencies in the final product and lead to production issues.
The following table summarizes the processing techniques and their key considerations:
| Processing Technique | Key Considerations |
|---|---|
| Injection Molding | Pre-drying, temperature and pressure settings, mold tightness |
| Extrusion | Drying conditions, temperature control, fiber and film production |
| Blow Molding | Temperature ranges, considerations for filled grades |
| Machining | Coolant selection, annealing process, achieving precision |
By understanding and optimizing these processing techniques, manufacturers can produce high-quality PPS parts and components for various applications.
When designing with PPS plastic, several factors must be considered to ensure optimal performance and cost-effectiveness.
Choosing PPS for a specific application requires careful evaluation of its unique properties.
Chemical Resistance
PPS's resistance to aggressive chemicals makes it suitable for applications in chemical processing and industrial equipment.
It withstands exposure to strong acids, bases, organic solvents, oxidizing agents, and hydrocarbons.
High-Temperature Stability
PPS is ideal for applications requiring continuous high-temperature resistance.
It can withstand temperatures up to 220°C (428°F) continuously and up to 260°C (500°F) for short periods.
Dimensional Stability
PPS maintains its dimensions even under high temperature and humidity conditions.
This stability is crucial for precision parts with tight tolerances.
PPS can be machined to close tolerances, making it suitable for complex, precision parts.
Machining can cause surface cracking and internal stresses in PPS.
These issues can be mitigated through annealing and the use of appropriate coolants.
Non-aromatic, water-soluble coolants, such as pressurized air and spray mists, are recommended for achieving high-quality surface finishes.
PPS maintains excellent dimensional stability across various temperatures.
It exhibits minimal dimensional changes with temperature variations.
This stability ensures reliable performance in varying environmental conditions.
While PPS offers excellent performance, it is more expensive than many standard engineering plastics.
Designers should evaluate the cost-benefit ratio of using PPS.
Alternative materials, such as PEEK, may be considered for less demanding applications.
However, PPS's unique combination of properties often justifies its higher cost in specific applications.
PPS is generally considered safe and non-toxic, but proper handling and safety protocols must be followed.
PPS can pose risks to human health and the environment if not handled properly or used inappropriately.
Proper safety protocols and guidelines should be followed to minimize risks.
PPS has poor UV resistance, making it unsuitable for outdoor applications without protective coatings.
The following table summarizes the key design considerations for PPS applications:
| Design Consideration | Key Points |
|---|---|
| Selecting PPS for Specific Applications | Chemical resistance, high-temperature stability, dimensional stability |
| Machining and Finishing | Annealing, appropriate coolants, surface cracking and internal stress mitigation |
| Dimensional Stability Across Temperatures | Minimal dimensional changes, reliable performance in varying conditions |
| Cost Considerations | Higher cost than standard plastics, cost-benefit evaluation, alternative materials |
| Environmental and Safety | Generally safe, proper handling and safety protocols, poor UV resistance |
PPS plastic offers exceptional versatility and high performance, making it ideal for demanding applications. Its chemical resistance, thermal stability, and mechanical strength ensure reliability across industries.
Understanding PPS’s modifications, processing methods, and design guidelines is crucial to maximizing its potential. With proper application, PPS creates durable products in automotive, aerospace, electronics, and more.
Tips: You maybe interested to the all plastics
| PET | PSU | PE | PA | PEEK | PP |
| POM | PPO | TPU | TPE | SAN | PVC |
| PS | PC | PPS | ABS | PBT | PMMA |
TEAM MFG is a rapid manufacturing company who specializes in ODM and OEM starts in 2015.